- Powerform® 18 is a high strength rotation resistant hoist rope.
- A sample of rope from each production batch is tested to destruction in order to confirm compliance with catalogue breaking force values.
- Good resistance to rotation verified by testing on the in-house torque/turn machine.
- Suitable for use on single part and multi-part hoist reeving systems.
- High fatique life resulting from unique compaction process.
- Increased resistance to crushing . Recommended for multi-layer spooling operations.
- Increased abrasion resistance resulting from the unique compaction process.
- Fully lubricated in manufacturing.
| Nom. Rope Dia. (mm) | Nom. Rope Dia. (in) | Approx. Mass (kg/100m) | Minimum Breaking Force | |||
|---|---|---|---|---|---|---|
| Galvanised & Ungalvanised | ||||||
| Rope Grade | ||||||
| 1960N/mm2 | 2160N/mm2 | |||||
| kN | tonnes | kN | tonnes | |||
| 6 | 17.5 | 29.4 | 3.0 | |||
| 7 | 23.8 | 38.0 | 3.9 | |||
| 8 | 31.0 | 51.8 | 5.3 | |||
| 9 | 39.3 | 64.6 | 6.6 | |||
| 10 | 48.5 | 80.8 | 8.2 | |||
| 11 | 58.7 | 101.0 | 10.3 | 111 | 11.3 | |
| 12 | 69.8 | 116.0 | 11.8 | 127 | 12.9 | |
| 1/2 | 78.2 | 135.0 | 13.8 | 148 | 15.1 | |
| 13 | 82.0 | 141.0 | 14.4 | 155 | 15.8 | |
| 14 | 95.1 | 160.0 | 16.3 | 177 | 18.0 | |
| 15 | 109.0 | 182.0 | 18.6 | 201 | 20.5 | |
| 16 | 5/8 | 124.0 | 209.0 | 21.3 | 232 | 23.6 |
| 17 | 140.0 | 237.0 | 24.2 | 262 | 26.7 | |
| 18 | 157.0 | 266.0 | 27.1 | 295 | 30.1 | |
| 3/4 | 175.0 | 291.0 | 29.7 | 322 | 32.8 | |
| 20 | 194.0 | 320.0 | 32.6 | 359 | 36.6 | |
| 22 | 235.0 | 379.0 | 38.6 | 424 | 43.2 | |
| 7/8 | 240.0 | 387.0 | 39.4 | 433 | 44.1 | |
| 24 | 279.0 | 462.0 | 47.1 | 523 | 53.3 | |
| 1 | 313.0 | 517.0 | 52.7 | 585 | 59.6 | |
| 26 | 328.0 | 542.0 | 55.2 | 613 | 62.5 | |
| 28 | 380.0 | 632.0 | 64.4 | 710 | 72.4 | |
| 30 | 437.0 | 721.0 | 73.5 | 809 | 82.5 | |
| 32 | 1-1/4 | 497.0 | 820.0 | 83.6 | 920 | 93.8 |
Note: Rope Sizes and Breaking Force not shown in the standard table, may be available on request and prior confirmation.